可靠性试验项目列表High Relibility Experiment List |
|||
Mumber序号 |
Experiment ltems 试验项目 |
Experiment Method And Comditions试验方法和条件 |
Reference参考文献 |
1 |
Soder Resistance Test 耐焊接热试验 |
260℃±5℃ for 10±2sec. Immerse body into solder 1/16"±1/32"将器件引线浸入熔融的260℃的焊料中10±2s,浸至距壳体1/16”±1/32”处 |
MIL-STD-750D METHOD-2031 |
2 |
Soderability Test 可焊性试验 |
245℃±5℃ for 5sec.245℃±5℃,5秒 |
MIL-STD-750D METHOD-2026 |
3 |
Pull Test 拉力试验 |
1Kg in Axial Lead direction for 10 sec.对引线施加1Kg力,保持10秒 |
MIL-STD-750D METHOD-2036 |
4 |
Bend Test 弯曲试验 |
0.5Kg Weight Applied To Each Lead Bending Arcs 90 ±5° For Three Times 用0.5Kg力对引线进行90±5度弯曲,共3次 |
MIL-STD-750D METHOD-1038 |
5 |
High Temperarure Reverse Bias Test 高温反偏试验 |
Ta=100℃ for 1000Hrs at Vr=80% Rated Vr在100℃的情况下,施加80%额定电压,1000小时 |
MIL-STD-750D METHOD-1051 |
6 |
Forward Operation Life Test 正向寿命试验 |
Ta=25℃ Rated Average Current 在25℃的情况下,通入额定电流,1000小时 |
MIL-STD-750D METHOD-1027 |
7 |
Intermittent Operation Life Test间歇工作寿命试验 |
On stat:5 min with Rate IRMS Power Off state :5 min with Cool Forced Air. On and Off for 1000 Cycles. 开态:额定功率5分钟, 关态:冷风吹5分钟,共1000循环 |
MIL-STD-750D METHOD-1036 |
8 |
Pressure Cooker Test高温蒸煮试验 |
15 PSIG, Ta=121℃,24hrs 15 PSIG,121℃,24小时 |
MIL-S-19500 APPENDIX C |
9 |
Temperature Cycling Test 温度循环试验 |
-55℃/+150℃ 30 Minutes For Dwelled Time 5 Minutes For Transfered Time.Total 10 Cycles. -55℃/+150℃,保持30分钟,转换时间5分钟,共20个循环 |
MIL-STD-750D METHOD-1051 |
10 |
Thermal Shock Test 热冲击试验 |
0℃ for 5 min,100℃ for 5Min,Total 10 Cycles. 0℃/5分钟 共10循环 |
MIL-STD-750D METHOD-1056 |
11 |
Forward Surge Test 正向浪涌试验 |
8.3 ms Sinhle Hale Sine-ware One Surge. 8.3毫秒 单向正弦半波 |
MIL-STD-750D METHOD-4066 |
12 |
Humidity Test 恒温恒湿试验 |
Ta=85℃,RH=85% for 1000hrs. |
MIL-STD-750D METHOD-1021 |
13 |
High Temperarure Storage Life Test 高温存储寿命试验 |
150℃ for 1000Hrs 150℃,1000小时 |
MIL-STD-750D METHOD-1031 |